A dielectric material conducts minimal electricity and provides an insulating layer between two conducting copper layers. The most common dielectric material is FR-4, but before selecting it for your board, you must carefully consider its properties.
Once you’re ready to choose a material, use the Sierra Circuits Material Selector tool to input criteria and get an easy-to-compare list of dielectrics with the right properties.
Glass Transition Temperature (Tg)
Glass transition temperature, or Tg, is the temperature range in which a PCB substrate transitions from a glassy, rigid state to a softened, deformable state as polymer chains become more mobile. When the material cools back down, its properties return to their original states. Tg is expressed in units of degrees Celsius (ºC).
Decomposition Temperature (Td)
Decomposition temperature, or Td, is the temperature at which a PCB material chemically decomposes (the material loses at least 5% of mass). Like Tg, Td is expressed in units of degrees Celsius (ºC).
A material’s Td is an important ceiling when assembling PCBs, because when a material reaches or surpasses its Td, changes to its properties are not reversible. Contrast this to Tg, glass transition temperature, where properties will return to their original states once the material cools below the Tg range.
Choose a material where you can work in a temperature range that’s higher than Tg but well below Td. Most solder temperatures during PCB assembly are in the 200 ºC to 250 ºC range, so make sure Td is higher than this (luckily, most materials have a Td greater than 320 ºC).
Coefficient of Thermal Expansion (CTE)
The coefficient of thermal expansion, or CTE, is the rate of expansion of a PCB material as it heats up. CTE is expressed in parts per million (ppm) expanded for every degree Celsius that it is heated.
As a material’s temperature rises past Tg, the CTE will rise as well.
The CTE of a substrate is usually much higher than copper, which can cause interconnection issues as a PCB is heated.
CTE along the X and Y axes are generally low – around 10 to 20 ppm per degree Celsius. This is usually thanks to the woven glass that constrains the material in the X and Y directions, and the CTE doesn’t change much even as the material’s temperature increases above Tg.
So the material must expand in the Z direction. The CTE along the Z axis should be as low as possible; aim for less than 70 ppm per degree Celsius, and this will increase as a material surpasses Tg.
The point at which the displacement is maximum on the CTE curve is referred to as glass transition temperature (Tg). If the temperature is higher than the Tg, the substrate softens and doesn’t expand any further.
Thermal Conductivity (k)
Thermal conductivity, or k, is the property of a material to conduct heat; low thermal conductivity means low heat transfer while high conductivity means high heat transfer. The measure of the rate of heat transfer is expressed in watts per meter per degree Celsius (W/M -ºC).
Most PCB dielectric materials have a thermal conductivity in the range of 0.3 to 0.6 W/M-ºC, which is quite low compared to copper, whose k is 386 W/M-ºC. Therefore, more heat will be carried away quickly by copper plane layers in a PCB than by the dielectric material.
Dielectric Constant or Relative Permittivity (Er or Dk)
Considering the dielectric constant of a material is important for signal integrity and impedance considerations, which are critical factors for high-frequency electrical performance. The Er for most PCB materials is in the range of 2.5 to 4.5.
The dielectric constant varies with frequency and generally decreases as frequency increases; some materials have less of a change in relative permittivity than others. Materials suitable for high frequency applications are those whose dielectric constant remains relatively the same over a wide frequency range–from a few 100MHz to several GHz.
Dielectric Loss Tangent or Dissipation Factor (Tan δ or Df)
A material’s loss tangent gives a measure of power lost due to the material. The lower a material’s loss tangent, the less power lost. The Tan δ of most PCB materials range from 0.02 for most commonly used materials to 0.001 for very low-loss high-end materials. It also varies with frequency, increasing as frequency increases. Read the difference between microstrip and stripline in PCBs.
Loss tangent isn’t usually a critical consideration for digital circuitry, except at very high frequencies above 1Ghz. However, it is a very important parameter for analog signals, as it determines the degree of signal attenuation and thus affects the signal to noise ratio at various points along signal traces.
Volume Resistivity (ρ)
Volume resistivity, or electrical resistivity (ρ), is one of the measures of the electrical or insulation resistance of a PCB material. The higher a material’s resistivity, the less readily it allows the movement of electric charge, and vice versa. Resistivity is expressed in ohm-meters (Ω-m) or ohm-centimeters (Ω-cm)
As dielectric insulators, PCB materials are required to have very high values of resistivity, in the order of 10⁶ – 10¹⁰ Megaohm-centimeters. Resistivity is somewhat affected by moisture and temperature.
Surface Resistivity (ρS)
Surface resistivity (ρS) is the measure of the electrical or insulation resistance of the surface of a PCB material. Like volume resistivity, PCB materials are required to have very high values of surface resistivity, in the order of 10⁶ — 10¹⁰ Megaohms per square. It is also somewhat affected by both moisture and temperature.
Electrical strength measures a PCB material’s ability to resist electrical breakdown in the PCB’s Z direction (perpendicular to the PCB’s plane). It is expressed in Volts/mil. Typical electrical strength values for PCB dielectrics are in the range of 800 V/mil to 1500 V/mil.
Electrical strength is determined by subjecting the PCB material to short high voltage pulses at standard AC power frequencies.
Flammability Specs (UL94)
UL94, or the Standard for Safety of Flammability of Plastic Materials for Parts in Devices and Appliances testing, is a plastics flammability standard that classifies plastics from lowest (least flame-retardant) to highest (most flame-retardant).
The standards are defined by Underwriters Laboratories (UL). Most PCB materials adhere to UL94 V-0; here are its requirements
1. The specimens may not burn with flaming combustion for more than 10 seconds after either application of the test flame.
2. The total flaming combustion time may not exceed 50 seconds for the 10 flame applications for each set of 5 specimens.
3. The specimens may not burn with flaming or glowing combustion up to the holding clamp.
4. The specimens may not drip flaming particles that ignite the dry absorbent surgical cotton located 300 mm below the test specimen.
5. The specimens may not have glowing combustion that persists for more than 30 seconds after the second removal of the test flame.
Moisture absorption is the ability of a PCB material to resist water absorption when immersed in water. It is given by a percentage increase in weight of a PCB material due to water absorption under controlled conditions as per standard test methods. Most materials have moisture absorption values in the range of 0.01% to 0.20%.
Moisture absorption affects the thermal and electrical properties of the material, as well as the ability of the material to resist conductive anode filament (CAF) formation when a PCB circuit is powered.
Methylene Chloride Resistance
Methylene chloride resistance is a measure of a material’s chemical resistance; specifically, the ability of a PCB material to resist methylene chloride absorption.
Just like moisture absorption, it is expressed by a percentage increase in the weight of a PCB material due to exposure to or soaking in methylene chloride under controlled conditions. Most PCB materials have methylene chloride resistance values in the range of 0.01% to 0.20%.
Michael J. Gay, Director, High-Performance Products, Isola Group, stated that “Moisture is one of the sources of Dk variation in PCB materials. There are other possible sources that could potentially result in some minor variation, but moisture uptake over time is a fairly large potential factor.” The below chart shows the moisture uptake in a 24-hour DI water soak at various temperatures for Tachyon 100G material.
Michael further explained, “As you can see, the Dk is about 0.02 higher after the material becomes saturated at 23 °C or room temperature. It is not a huge difference, but might make you think of changing the line width requirement to center the impedance. Moisture uptake would happen to the clad laminate over many weeks or to the etched laminate over several hours. Uptake is dependent on the length of the path for the material to reach equilibrium. For example, a single etched signal layer core sitting in AOI for a few hours would pick up the maximum moisture content at RT (relative temperature). These areas are usually about 60% RH (relative humidity) and so moisture is readily available.”
In an actual PCB design, the moisture may not stay in the areas near hot components and be driven out of the board when temperatures reach 80-90 °C near hot chips.
- The sample was pulled from the water soak and then equilibrated for 4 hours before -40 °C reading.
- Each subsequent reading was taken after equilibration of 150 minutes at a new temperature.
Key takeaways of the experiment:
- Dk response as expected: It increases as water transitions through phases and then decreases as moisture is driven off from the sample.
- Df response also as expected: A slow increase in loss due to the same phase transitions in the retained moisture, followed by a decrease as the moisture is driven off.
- Additional testing could be supported with different test conditions.
Michael also likes to add, “For high-speed design, we recommend that materials are dry prior to lamination using a baking process. Materials like Tachyon 100G, moisture does not negatively influence curing, but as you can see, moisture does result in Dk shifting.”
For conveyorized oxide replacements, an efficient dryer at the end of a conveyorized oxide replacement line should remove all moisture from the inner layer surface. However, drying on layers for 30 minutes at 100°C or higher is considered a best practice, especially for the boards subjected to lead-free processes. Drying in racks is preferred.
For other materials, especially epoxy-based resin systems, moisture can also impede the cure reaction and result in lower thermal resistance and thermal properties. We recommend baking inner layers to avoid this problem.
On the finished board of all material, you will see a similar variation in Dk if the boards are not dry. All polymeric materials pick up moisture. The reason that moisture causes problems is that it is a polar molecule and interferes with the magnetic fields in the local vicinity. This is the very reason why some resins are higher loss and some are lower loss – polarity of the resin molecules. For instance, PTFE is a very low polarity resin and is a low-loss material.
Michael concluded, “Moisture can easily find its way through the resin molecules and park between them because it is so small. The amount of water a plastic can absorb is a result of the amount of free space in the cured resin. Some have more free space than others.”
Peel strength is a measure of the bond strength between the copper conductor and the dielectric material. It is expressed in pounds of force per linear inch (PLI, or average load per conductor width) required to separate bonded materials where the angle of separation is 180 degrees.
Peel strength tests are done on samples of copper traces of 1 OZ thick and ~ 32 to 125 millimeters wide after standard PCB manufacturing processes. It is completed under 3 conditions:
• After thermal stress: after a sample is floated on solder at 288 ºC for 10 seconds
• At elevated temperatures: after a sample is exposed to hot air or fluid at 125 ºC
• After exposure to process chemicals: after a sample is exposed to a specified series of steps in a chemical or thermal process
Flexural strength is the measure of a material’s capability to withstand mechanical stress without fracturing. It is expressed in either Kg per square meter or pounds per square inch (KPSI).
Flexural strength is generally tested by supporting a PCB at its ends and loading it in the center. IPC-4101 is the Specification for Base Materials for Rigid and Multilayer Printed Boards, and it gives the minimum flexural strength of various PCB materials.
Young’s modulus, or tensile modulus, also measures the strength of a PCB material. It measures the stress/strain ratio in a particular direction, and some PCB laminate manufacturers give strength in terms of Young’s modulus instead of flexural strength. Like flexural strength, it is expressed in force per unit area.
Some PCB laminate manufacturers give the PCB materials strength not in terms of Flexural Strength but in terms of Young’s modulus which is a measure of Stress/strain ratio in a particular direction.
The density of a PCB material is expressed in grams per cubic centimeter (g/cc) or pounds per cubic inch (lb/in^3).
Time to Delamination
Time to delamination measures how long a material will resist delamination—the resin’s separation from the laminate, foil, or fiberglass – at a specified temperature. Delamination can be caused by thermal shock, the wrong Tg in the material, moisture, a poor lamination process.
For more help selecting the right PCB material, use the Sierra Circuits Material Selector tool. Input a specific material property or properties, and the tool will give you a list of materials that meet them. An easy-to-use comparison table lets you compare the detailed properties of up to five materials.
To learn more about PCB material selection, watch our webinar PCB Material Selection: Electrical and Manufacturing Considerations.
澳洲5结果9 Chapters - 30 Pages - 40 Minute Read
- Basic properties of the dielectric material to be considered
- Signal loss in PCB substrates
- Copper foil selection
- Key considerations for choosing PCB materials
About the author: Atar Mittal is the Director and General Manager of design and assembly division at Sierra Circuits. He is responsible for the design and development of strategies and process automation tools for complex printed circuit boards and assemblies. Atar is also currently engaged in the development of productivity tools for electronics designers that would have a tremendous impact on shortening the development time.